Physical Properties:
1) Compressive strength
| Direction | 200 MCI | 400 MCI |
A (minimum) | 15.0 MPa | 15.0 MPa |
B (minimum) | 1.5 MPa | 1.5 MPa |
C (minimum) | 0.2 MPa | 0.2 MPa |
Specimen dimensions Φ25.4 mm, length 25.4 mm from direction A, B and C, where
Speed: 1mm/min | ||
2) Porosity/water absorption
| Item | 200 MCI | 400 MCI |
Minimum | 18.6% | 17.8% |
Maximum | 23.4% | 20.7% |
Average (n>5 per lot) | 22.1% | 19.6% |
Total pore volume | 0.18-0.24 (cm3/g) | 0.18-0.24 (cm3/g) |
3) Bulk density
| 100 MCI | 0.46 g/cm3±15% |
200 MCI | 0.43 g/cm3±15% |
300 MCI | 0.50 g/cm3±15% |
400 MCI | 0.48 g/cm3±15% |
4) Coefficient of Thermal Expansion
| Item | 200 MCI | 400 MCI |
Heating rate | 5C/min, 20C…1000C | 5C/min, 20C…1000C |
Average | 1.5*10-6K-1 | 1.8*10-6K-1 |
5) Thermal Conductivity
1.5…1.6 W/mk at temperature 25C…600C
6) Specific Heat Capacity
At:100C/200C/300C
800KJ/Kg950KJ/Kg2000KJ/Kg
7) Continuous High Temperature Durability
Maximum shrinkage of length after 100 hours at 1200C
200MCI 400MCI
Maximum:0.5% 0.1%
8) High Temperature Stability
Maximum shrinkage after 100 hours at 1450C
200 MCI400 MCI
Maximum2.0%2.5%
9) Gas Flow Resistance
Flow speed 16m/s200 MCI400 MCI
Pressure drop {10-2mmAg/mm} 60130
10) Structural Integrity to Thermal Shock
(Cooling with water)
Cracks start at approx. 800C
No destruction of ceramic bodies until approx. 1180C
11) Softening temperature
Definition: temperature, at which the instantaneous rate of thermal expansion is zero.
Procedure: analogous to coefficient of thermal expansion; determination with extrapolation.
Minimum: 1380C
Chemical Composition:
| Item | Stoneware | Cordierite | Mullite- Cordierite | Mullite |
| SiO2 | 69~71 | 46~48 | 29~30 | 27~28 |
| Al2O3 | 18~20 | 34~37 | 68~69 | 70~71 |
| MgO | 0.15~0.20 | 7.00~7.50 | --- | --- |
| K2O.Na2O.CaO | 3.00~3.30 | 2.50~2.90 | 0.70~0.90 | 0.80~1.20 |
| Fe2O3 | 0.70~0.90 | 0.70~0.90 | 0.50~0.70 | 0.50~0. |
We promise to reply you in 24hours, OEM & ODM service for your unique idea with absolute convenience. We value our business credit, promise to keep your company information confidential.If any inquiry or problem.Please feel free to contact with me.
Grace Zhang
Whatsapp/TEL:008613767885030
QQ: 84781705
Skype: yakegrace
Wechat: xz9426
TM: cn1000900349
Q: What is your MOQ?
A: Our product MOQ is 1000kg&1m³
Q: What is the delievery time?
A: It takes aroud 10-15days for one 20" container.
Q: What is the shipping port?
A: Shanghai,Shenzhen,Qingdao.
Q: What is payment terms?
A: T/T,L/C, West Union.
Q: What information should I offer to you if I want to know the price?
A: Appication/usage,Size,Material,Quantity,Package term,Delievery time,Payment term,Destination.
Q: What is your warranty?
A: By National Standard GBT 10504-2008, Offer lifetime consultation on problems occurred.
Why choose products from KANGYU ?
1. Specialize in this field for more than 10 years.
2. More than 1000 workers, Strong ability of production.
3. Shorter delivery time.
4. Rich variety of products:molecular sieve,random and structured chemical packing in ceramic,plastic&metal honeycomb ceramics,inert ceramic balls,activated alumina,alumina grinding balls,expanded perlite,porous ceramic filter pipe and so on.
5. Competitive price,modern appearance.
6. Do any sticker you need(OEM,ODM).
7. Going green and environmental protection:No mercury, No radition, No UV.
8. Honesty is the most important
We Specialized in Manufacturing molecular sieve, random and structured chemical packing in ceramic, plastic & metal, honeycomb ceramics, inert ceramic balls, activated alumina, alumina grinding balls, etc.
We has an annual manufacturing capacity of 5000 ton molecular sieves, 20000 m3 of varieties types of chemical packings, 3000 m3 of honeycomb ceramics and 5000 m3 of inert ceramic balls, 2000 ton activated alumina etc.
Welcome to our factory and negotiate business. We trust we will be your best supplier in China.